Benefits:
- Very high chemical resistance
- Hygienic – Easy to clean, maintain and sterilise; minimal joints
- Heat resistant to 120*C @ 9mm
- Steam cleanable
- Non-tainting and non-dusting
- High abrasion resistance
- Withstands high mechanical stress
- Low odour during application
- Positive slip resistance
FeRFA Resin Flooring guidelines
Description:
Applied in two or more coats. Generally solvent or water borne.
Duty:
light foot traffic, occasional rubber tyred vehicles.
Typical Thickness:
up to 150 µm
Description:
Applied in two or more coats. Generally solvent free.
Duty:
light foot traffic, occasional rubber tyred vehicles/regular foot traffic, frequent fork lift truck traffic, occasional hard plastic-wheeled trolleys
Typical Thickness:
150 µm to 300 µm
Description:
Applied in two or more coats. Generally solvent or water borne.
Duty:
lregular foot traffic, frequent fork lift truck traffic, occasional hard plastic-wheeled trolleys
Typical Thickness:
300 µm to 1000 µm
Description:
Aggregate dressed systems based on multiple layers of floor coatings or flow-applied floorings, often described as ‘sandwich’ systems.
MD/HD
Duty:
regular foot traffic, frequent fork lift truck traffic, occasional hard plastic-wheeled trolleys/constant fork lift truck traffic, hard plastic wheeled trolleys, some impact
Typical Thickness:
> 2 mm
Description:
Often referred to as ‘self-smoothing’ or ‘self-levelling’ flooring and having a smooth surface.
Duty:
regular foot traffic, frequent fork lift truck traffic, occasional hard plastic-wheeled trolleys/constant fork lift truck traffic, hard plastic wheeled trolleys, some impact
Typical Thickness:
2 mm to 3 mm
Description:
Trowel-finished, heavily filled systems, generally incorporating a surface seal coat to minimize porosity.
Duty:
regular foot traffic, frequent fork lift truck traffic, occasional hard plastic-wheeled trolleys/constant fork lift truck traffic, hard plastic wheeled trolleys, some impact
Typical Thickness:
> 4 mm
Description:
Having a smooth surface.
Duty:
constant fork lift truck traffic, hard plastic wheeled trolleys, some impact/severe heavily loaded traffic and impact
Typical Thickness:
4 mm to 6 mm
Description:
Trowel-finished, aggregate filled systems effectively impervious throughout their thickness.
Duty:
severe heavily loaded traffic and impact
Typical Thickness:
> 6 mm
Product: Pagefresh HF Finish: Matt
Thickness: _ mm (6-9 mm)
Preparatory work and application in accordance with contractors instructions.
Supplier/ Installer: Page Industrial Coatings Ltd Telephone: Customer Service +44 (0) 1443 475270
Substrate Requirements: Concrete or screed substrate should be a minimum of 25 N/mm2, free from laitance, dust and other contamination. The substrate should be dry to 75% RH as per BS8204 and free from rising damp and ground water pressure.
A special Pagefast Primer can be used for substrates up to 100% RH (surface dry)
For areas where continual heat resistance (above 50 degrees) is critical use Pagefresh primer. Pagefresh primer is also suitable for substrates up to 97% RH, please consult the Product datasheet for further details.
The priming process may be omitted when applying Page HF over lsopol SBR screed, or when consistency of the concrete base ensures minimal porosity, is free of voids and is surface dry up to 97% RH.
Primer: (if Required) Page Prime @ 0.25kg/m2 (porous substrate may require 2 coats)
OR: where a dpm is required,
Page Hydraseal DPM @ 0.5 kg/m2 OR: where high heat resistance is critical
Pagefresh primer @ 0.25 kg/m2 Scatter: 1-2mm silica sand @ 0.5 kg/m2
Topping: Page HF (density 2.1 kg/I)
For general chem. Resistance-12.6 kg/m2@ 6mm For best temp resistance-18.9 kg/m2@ 9mm
Detailed application instructions are available upon re quest.
Installation Service
This installation is carried out by Page Industrial Coat ings approved applicator all Resin and accredited member of FERFA.
The finished systems is assessed as non hazardous to health and the environment. The long service life and seamless surface reduce the need for repairs, mainte nance and cleaning. Environmental and health consid erations are controlled during manufacture and application of the products by Page Industrial Coatings and staff are fully trained and experienced employees.
The figures that follow are typical properties achieved in laboratory tests at 20 degrees and at 50% Relative Humidity.
| EN 13813 A1.0-B2.8-I R20.0 Synthetic screed material for use internally in buildings | ||
|---|---|---|
| Reaction to fire | Bs S1 | (13501-l) |
| Impact Resistance | IR 20.0 | (EN ISO 6272) |
| Wear Resistonce | A 1.0 | (EN 13892-3) |
| Boned Strength | B2.8 | ((EN 13892-8)) |
| Slip Resistadlce Method described in in BS 7976-2 (typical values for 4-S rubber slider) |
Dry >40 low slip potential (in accordacnce with I-ISE and UKSRG guidelines) |
The slipperiness of flooring materials can change significanlly, due to the installation process, after short periods of use, due to inappropriate maintenance, longer term wear and/ or surface contaminants (wet or dry).
Textured systems are recommended to meet slip resistance value requirements for wet conditions and/ ,or surface contaminants (wet or dry) – please contact our technical Advisors for further details and specifications.
| Temperature resistance | Tollerant to intermittent spillages up to 120°C or sustained dry heat from -A40°C to 105°C (at 9 mm thickness.) |
| Water Permeability | Nil – Karsten test (impermeable) |
| Vapour Permeability | ASTM E96 :9 0 3g/m’/ 2.4hrs(at 9 mm thick)(impermeable) |
| Chemical Resistance | Contact technical department – excellent resistance to sugars and most acids (organic and inorganic) |
| Compressive strength | > 50 N/mm2 (BS 6319) |
| Flexural Strength | 20 N/mm2 (BS 6319) |
| Tensile Strength | 10 N/mm2 (BS 6319) |
Speed Of Cure
| 10°C | 20°C | 30°C | |
| Light Traffic | 36 hours | 24 hours | 12 hours |
| Full Traffic | 72 hours | 48 hours | 24 hours |
| Full Chemical Cure | 10 days | 7 days | 5 days |
Aftercare – Cleaning and Maintenance
Clean regularly using a single or double headed rotary scrubber drier in conjunction with a m ild alkaline detergent.